Poliüretan ipək mat lak


  Two pack, polyurethane based ,silk-matt, mainly developed for wooden surfaces.  Highly resistant to abrasion, water, stains and detergents. Recommended  for floors, new or bare wood or already varnished wood. Exceptional resistance to wear, knocks and abrasion.



Wooden surfaces for all architectural purposes, carpentry work, furniture , Floors, doors, trim, woodwork, cabinets, furniture, prefinished panels etc.


  Colour                                              hazy

    Gloss level                                       Silk matt20-40%

      Volume Solids                       43  % by volume, 46%  by weight

      Typical Film Thickness               30-40  microns dry ( 68-92   microns wet)

      Theoretical Coverage                 12-16  m²/litre

     Practical Coverage                     Allow appropriate loss factors

      Method of  Application               Spray,  brush, roller




   Overcoating Interval with 

 recommended topcoats

Temperature                      Touch  Dry             Hard Dry               Minimum            Maximum                               


10  °C                             1 hours                      36 hours                4 hours            not limited

15  °C                             45 minutes                 30 hours               3  hours           not limited     

25 °C                              30 minutes                 24 hours                2 hours            not limited 




VOC                                                             540 gr/lt  (UK-PG6/23(92))

Product Weight                                          Mixed   - 0.99±0,02 g/l

Flash point                                                  Mixed  4°C

Viscosity (25 0C , din cup 4, sec)    230-240 sec



Before application, the surface should be sound, clean and free  from oil, grease, loose particles, dust, etc.   Application can be done by the recommended application methods.



  Material is supplied in 2 containers as a unit. Always mix a complete unit in the proportions supplied. Once the unit has been mixed, it   must be used within the working pot life specified.

   (1)  Agitate Base (Part A) with a power agitator.

   (2)  Combine entire contents of Curing Agent (Part B) with Base (Part A) and mix  thoroughly with power agitator


 Mix Ratio     

2.13 Part A to 1 Part B   by volume

2 Part A to 1 Part  B        by weight


  Working Pot Life


3 hours             



 CORELLA Thinner T 36    ( 4~5% )

 DO NOT thin more  than allowed by local   environmental legislation.



CORELLA Thinner T 82


Work Stoppages and Cleanup

Do not allow material to remain in hoses, gun or spray equipment. Thoroughly flush all equipment with

CORELLA Epoxy Thinner  T82. Once units of paint have been mixed they should not be resealed and it is advised that afterprolonged stoppages work recommences with freshly mixed units.

Clean all equipment immediately after use with CORELLA Epoxy Thinner  T82.



Symbol: Xn, F

Risk notifications: R 10/20/22/36/37/38/51

Safety notifications: S 2/3/7/9/16/25/29/46




               Part A                                         Part B

Nett                   Pack                       Nett                  Pack

12 kg                 15 L                     6 kg                       3 L *2

Total weight after packing: 20 kg


Shelf Life      36  months minimum at 5-35°C. Store in dry, shaded conditions away from sources of heat and ignition.